1, The repairing agent is made of fabric and has better repairing effect with glass lined special reinforcing belt.
2, The maximum temperature of the repair agent is 250 ºC
3, It can resist general inorganic acid, organic acid, alcohol, alkali, amine, etc. For example: 30% hydrochloric acid, 30% nitric acid, carbonic acid, 10% hydrobromic acid, 20% nitric acid, 20% phosphoric acid, 30% sulfuric acid, 30% ammonia water, lime water, 40% potassium hydroxide, 40% sodium hydroxide, propanol, butanol, glycol, diethyl hydrogen salt, methylamine (water content 75%), bicarbonate, mineral
4, Weight: 1000g
5, The abrasion resistance shall be in accordance with ASTM D4060 60mgm / 1000 rpm
6, Salt spray resistance according to ASTM B117 has no effect for 10000 hours
7, The adhesion shall be in accordance with ASTM d1002 105kg / cm2 (20 ºC) 112kg / cm2 (100 ºC)
8, The impact strength is in accordance with ASTM G14 2.2joules
9, Compressive strength according to ASTM d695 510kg / cm2
10, According to ASTM D790 350kg / cm2
11, Heating and curing: in order to achieve the best performance of the product, after using xy406, let it last for more than 4 hours at the temperature of 80 ºC, which can make the internal reaction sufficient to achieve the best chemical resistance effect.
12, Mixing ratio: weight mixing ratio: 8.82:1 (base material: curing agent), brushing area after mixing (thickness: 0.4mm): 1.5kg, brushing area after mixing is 2.25m2
Storage period: at 0 ºC - 30 ºC, the base material and curing agent shall be stored separately, and the storage period shall be at least 3 years.
Scope of application: it is used to protect metal and ceramic protection system damaged by chemical substances, with strong chemical corrosion resistance. It has high temperature property for cold welding repair, and is suitable for effective protection of metal and cement matrix with high temperature and strong acid, solvent and chemical corrosion.
Schedule: operation and curing schedule
The temperature is 15 ºC 20 ºC 30 ºC
Machining or light load: 12 hours - 8 hours - 4 hours
Soak in chemicals for 7-5-3 days
2, The maximum temperature of the repair agent is 250 ºC
3, It can resist general inorganic acid, organic acid, alcohol, alkali, amine, etc. For example: 30% hydrochloric acid, 30% nitric acid, carbonic acid, 10% hydrobromic acid, 20% nitric acid, 20% phosphoric acid, 30% sulfuric acid, 30% ammonia water, lime water, 40% potassium hydroxide, 40% sodium hydroxide, propanol, butanol, glycol, diethyl hydrogen salt, methylamine (water content 75%), bicarbonate, mineral
4, Weight: 1000g
5, The abrasion resistance shall be in accordance with ASTM D4060 60mgm / 1000 rpm
6, Salt spray resistance according to ASTM B117 has no effect for 10000 hours
7, The adhesion shall be in accordance with ASTM d1002 105kg / cm2 (20 ºC) 112kg / cm2 (100 ºC)
8, The impact strength is in accordance with ASTM G14 2.2joules
9, Compressive strength according to ASTM d695 510kg / cm2
10, According to ASTM D790 350kg / cm2
11, Heating and curing: in order to achieve the best performance of the product, after using xy406, let it last for more than 4 hours at the temperature of 80 ºC, which can make the internal reaction sufficient to achieve the best chemical resistance effect.
12, Mixing ratio: weight mixing ratio: 8.82:1 (base material: curing agent), brushing area after mixing (thickness: 0.4mm): 1.5kg, brushing area after mixing is 2.25m2
Storage period: at 0 ºC - 30 ºC, the base material and curing agent shall be stored separately, and the storage period shall be at least 3 years.
Scope of application: it is used to protect metal and ceramic protection system damaged by chemical substances, with strong chemical corrosion resistance. It has high temperature property for cold welding repair, and is suitable for effective protection of metal and cement matrix with high temperature and strong acid, solvent and chemical corrosion.
Schedule: operation and curing schedule
The temperature is 15 ºC 20 ºC 30 ºC
Machining or light load: 12 hours - 8 hours - 4 hours
Soak in chemicals for 7-5-3 days